All Products

David from Canada

Our company import the bronze gleitlager from viiplus china,viiplus professional team makes sure customs clearance is always smooth. They provide an accurate bronze bushing classification, handle all the paperwork,We have received the self-lubricating bronze bushings. They look well done and the high quality.
Valerie from California

We import the bronze gleitlager from China to under the incoterm FOB shanghai, sometimes by Air. viiplus is a very good bronze gleitlager supplier, they are very professional and patient, after we inform the new order, they will manufacturer bronze gleitlager in time and give us the schedule , and then we just need to receive the bronze parts
Daisy From Germany

The best surface finishes for Sleeve Bearing, tighter concentricity, and bronze bushings material uniformity. The good supplier of standard inch and metric sleeve bearings and bushings from china. https://www.bronzelube.com/
Beverly from Florida

“Valve Bushings perfect,Thank you so much for your superior customer service! The steel-backed, PTFE lined rolled bushings are a low cost, a general-purpose product that provides excellent wear characteristics at high loads and speeds over a wide temperature range. They are designed to be self-lubricating and maintenance-free.
Michael Russo

The wrapped bronze bushings is produced with diamond-shaped lubrication indents on the inner diameter surface which provide lubricant reservoirs that allow for prolonged service.

Contact Person : Tiffany

Tin Plating Composite Bearing Material CM1 Guide Bushing

Place of Origin	Plain Bearing Material
Brand Name	China Plain-Bearing
Certification	DIN 1494/ISO 3547
Model Number	Wrapped composite sliding bearing
Minimum Order Quantity	500 Piece/Pieces
Price	flat strip material inch sizes Manufacturers,Factory Price
Packaging Details	Shipment Bushing Packing: Cartons per Wooden Case or Pallet.
Delivery Time	15~20 Days
Payment Terms	TT IN ADVANCE
Supply Ability	1000000 Piece/Pieces per Month Plain-Bearing Bushing

Contact me for free samples and coupons.

Whatsapp:0086 18588475571

Wechat: 0086 18588475571

Skype: sales10@aixton.com

If you have any concern, we provide 24-hour online help.

Product Details

Features	Low-maintenance, Lubricated Applications	Meterial	Composite Material Porous Bronze + Strips
Plating	Tin Or Copper	Type	Composite Material 3 Layer Strips
Finishing	Tin Plated, Brass Plated	Application	Printing And Dyeing Machines, And Machines Used In The Ocean Industry, Etc.
Bearing Bushing Factory Price	Tiffany@viiplus.com	Self-lubricating Bearing Bushing Manufacturer	Https://www.viiplus.com/
Bush Bearings Manufacturers Suppliers Exporters	Plain Bearings. Long, Maintenance-free Service, Manufactures Bushings In Various Designs And From Different Materials. Tiffany@viiplus.com, Bushings - Configure And Purchase - Https://www.viiplus.com/
High Light	CM1 Guide Composite Bearing Material , Tin Plating Bronze Bushing Material , Bushing Composite Bearing Material

Leave a Message

Product Description

Composite Bearing Material CM1 -Guide Bushing

Tin-Plated Composite Bearing Material CM1 Guide Bushing is a high-performance bearing component that combines the advantages of tin plating, composite material, and (Polytetrafluoroethylene) bushing. The tin plating provides excellent corrosion resistance and enhances the surface hardness of the bearing, while the composite material ensures strength and durability. The bushing, known for its low friction and high wear resistance, further improves the overall performance of the bearing. This combination results in a bearing that is suitable for a wide range of applications, especially those requiring high reliability and long service life.

Bushing Material, Composite Material CM1, metal-polymer self-lubricating plain bearings metal-polymer self-lubricating plain bearings. A unique, composite bearing material, a composite strip material made up of three layers: bronze, porous bronze, and : it is also available, on special order, with a non-indented bearing strip surface, available thickness: 1.0mm, 1.5mm, 2.0mm,2.5mm, Flat Strip Material Metric Size,

based according to ISO 3547 type P1
Negligible stick-slip effect

CM1 - This is a composite material consisting of three layers
A bronze backing strip and a sintered interlocking porous matrix,
impregnated and overlaid with a /lead mixture

Material type, based according to ISO 3547 type P1. Composition, Steel back with a sintered layer of tin bronze. Pore filling and cover layer

STEEL BACKED LINED

bearing strip material
Steel-Backed -Lined Sleeve Bearings ...
Steel-Backed Lined Sleeve Bearings, METRIC Are Used For Heavy Load, Moderate Speed Or Light Load, High Speed Applications.

Custom Made Plain/Sliding Bearings, manufacture of bearing bushes, flanged bushes, half-shells, and more

composite strip material made up of three layers: steel-backed or bronze backed, porous bronze, and acetal resin polymer:

Properties of Composite Materials for Secondary Sliding Surfaces

B.1 Composite Material CM1

This is a composite material consisting of three layers; a bronze backing strip and a sintered

interlocking porous matrix, impregnated and overlaid with a lead mixture.

The material shall conform to the characteristics listed in Table B.1 In addition, the condition of the material and its surface finish shall be checked visually.

Table B.1 Characteristics of CM1

Bronze backing material: CuSn 6

composition by mass Sn 5 to 7.50

P 0.35

Pb 0.10

Fe 0.10

Zn +Ni 0.50 %

others 0.30

Remainder Cu

(2.1 0.15) mm thickness

hardness HB -ISO 6506 (all parts) material: CuSn 10

Composition by mass

80 to 160

Bronze interlayer

Sn 10 to 12

Pb 1.00

P 0.25 to 0.4 %

Si 0.17

Fe 0.15

Ni 0.15

others 0.50

25 saturation with

thickness

.15

0.25 0.0 mm

Composite material material: + Pb Pb 49% to 62%,

Surface layer composition by mass remainder

0.01 +0.02

0.0 mm

Thickness

2578 2048 0.015 mm total thickness

Overlay adhesion-ISO 2409

minimum GT2

B.2 Composite Material CM2

The material shall consist of a flexible metal mesh which is sintered into a compound

with the bearing or sliding surface having the thicker coat. The metal mesh shall be CuSn6 stabilized mesh from 0.25 mm diameter wires which are

linked at intersections and which has a thickness after calendaring of approximately 0.4 mm.

The mesh count in warp and weft direction shall be 16 t 1 per 10 mm.

The compound shall be with 30 percent t 2 percent filler content, consisting of

glass fibers and graphite.

The material is to conform to the characteristics listed in Table B.2.

In addition, the condition of the material and its surface finish shall be checked visually.

Table B.2 Characteristic of CM2

Density 4100 kg/m to 4400 kg/m

Tensile Strength >45 MPa

Elongation 10 %

Thickness (0.48t 0.02) mm

Overlay adhesion minimum GT2

ISO 2409

Cylindrical bushes Flanged bushes Thrust washers Flanged washers Strips

Strip composite bearing bushing

Material composition

Strips Material composition

Strips are available in steel backed or bronze backed: